location:Home > turntable bearingNews > The material factors affecting the life of roller parts

Products
COLUMN NAVIGATION
One Way Backstop Bearing
Self-Aligning Ball Bearing
Lightweight Spherical Roller Bearing
36 Class Spherical Roller Bearing
35 Class Spherical Roller Bearing
Black-Horn Lmported Pprocess Bearing
Deep Groove Ball Bearing
KA Nylon Retainer Bearing
Deep Groove Ball Bearing
More models
Shandong Xinkaite Bearing Co.,Ltd.
Unified Social Credit Code: 9137 1525MA3C 5428XP
Production Department
Address: Xu Village Industrial Garden, Gan Town, Guan County, Shandong
Tel: +86 635 5638235
Fax: +86 635 5638808
Mobile: +86 15563545668
Service Hotline: 4000 305204
Sales Department
Address: 314 Puli Mansion, Beixiaoxinzhuang West Street, Jinan City, Shandong
Tel: +86 15562637177
Fax: +86 531 87901699
WhatsApp: +86 15688862750
Skype: live:XinKaite
Email: xkte@xinkaite.com
The material factors affecting the life of roller parts
Clicks:18414 Date:5-6
The material factors affecting the life of roller parts, austenite of high carbon chromium steel after quenching by normal, can contain 8%~20%Ar (residual austenite). Yanshan Mingschin conveying machinery manufacturing Co., Ltd. is a specialized production roller parts enterprises, mainly the production and supply of roller bearings, roller parts, KA bearings, 0 types of deep groove ball bearings, bearing agent manufacturers, low noise motor bearings, bearings and set off running in period.
Roller parts in Ar has its advantages and disadvantages, in order to promote, the content of Ar should be appropriate. Because the amount of Ar is mainly related to the condition of quenching and heating, the amount of Ar will affect the amount of carbon in the quenched martensite and the amount of undissolved carbide, and it is difficult to reflect the influence of the amount of mechanical properties. For this reason, the fixed austenite condition was used to obtain the different Ar amount by using the method of thermal stabilization of austenite. The effect of Ar content on the hardness and contact fatigue life of GCr15 steel after quenching was studied. In the actual operation, the supporting parts of the roller assembly of the Ming Xin conveying machine have the important advantage and the performance, the internal content and the ingredient can have the different function, in the use according to the certain standard.
With the increase of austenite content, hardness and contact fatigue life was increased, and then decreased after reaching the peak, but the peak value of Ar content of different hardness peak appeared at about 17%Ar, and the contact fatigue life of the peak at around 9%. When the test load is reduced, the influence of Ar on the contact fatigue life decreases. This is because when the amount of Ar has little effect on the strength reduction, the effect of toughening is obvious. Support and cause some defects and fittings for use in a manner that is at a low load, Ar had small amount of deformation, which reduce the stress peak, and the Ar processing has been strengthened and deformation stress strain induced martensite transformation and strengthening. However, when the load is large, the larger plastic deformation of Ar and the matrix will produce stress concentration and rupture, which will reduce the life. It should be noted that the beneficial effect of Ar must be in the Ar stable state, if the spontaneous transformation of martensite, the toughness of the steel will be reduced and brittle.
Roller accessories in the elements and content for the use of the advantages and disadvantages, for use in accordance with certain standards and forms of use.
Previous article: Method for preventing rust of stamping bearing seat      Next article: The role of roller bearing equivalent static load
Recommended reading
Roller bearing seat repair process and speed limit 2017.4.19
What are the core parts of roller accessories 2017.4.27
How do we carry on the maintenance to the roller bearing 2017.4.27
Recommended products
bearing 6310 C4 for idler
bearing 6310 C4 for idler
bearing 6309 C4 for idler
bearing 6309 C4 for idler
bearing 6308 C4 for idler
bearing 6308 C4 for idler
bearing 6307 C4 for idler
bearing 6307 C4 for idler
Home | About us | Products | Models | News | Honor | Substation | Message | Contact us
  China Shandong Xinkaite Bearing Co.,Ltd.turntable bearing professional manufacturers, long-term supply of turntable bearing, provide the latest turntable bearing price for roller bearings, roller parts industry concentrated areas, we have long-term fixed partners, its turntable bearing products further around the world. Sales hotline: 086+ 0635-5638235
Shandong Xinkaite Bearing Co.,Ltd.   Phone: +86 6355638235   Fax: +86 635 5638808   Email: xkte@xinkaite.com